CONSISTENCY OF FLY ASH QUALITY FOR MAKING HIGH VOLUME FLY ASH CONCRETE

Antoni Antoni, Alvin Krisnanta Widianto, Jerry Lakshmana Wiranegara, Djwantoro Hardjito

Abstract


Fly ash is a by-product of coal burning and is widely used as a substitute for cement material. The advantages of using fly ash in concrete include the improvement of workability and reduction of bleeding and segregation. The problem often encountered when using fly ash is the uncertainty of the fly ash quality. The quality is influenced by the coal origin, burning technique, mineral content, and capturing method. In this study, the consistency of fly ash from one power plant source was investigated for making a high-volume fly ash (HVFA) mortar. Variations in fly ash can be detected by applying rapid indicators as suggested in this paper; i.e., the pH of the fly ash in aqueous solution, the percentage of fly ash particles passing sieve #325 and the superplasticizer demand for the targeted slump flow. The fly ash replacement ratio was varied from 10–60% of cement, by mass. The results showed a large variation in the chemical content of the fly ash as shown by variation in pH, whereas only slight variation in the physical properties of the fly ash, i.e. particle size and shape. Superplasticizer demand for the same flow diameter was reduced with the increase of fly ash content, whereas the optimum fly ash replacement ratio for maximum strength varied among fly ash from different sampling periods. The compressive strength could reach that of control specimens at a replacement ratio of 20–30%, and mortar compressive strength of 42 MPa was still achievable at a replacement ratio of 50%.


Keywords


Fly ash, pH, HVFA, LOI, setting time, compressive strength

Full Text:

PDF

References


Ahmaruzzaman, M. 2010. A Review on the Utilization of Fly Ash. Progress in Energy and Combustion Science. 36: 327-363.

Blissett, R. S., and Rowson, N. A. 2012. A Review of the Multi-Component Utilisation of Coal Fly Ash. Fuel. 97: 1-23.

Deo, S. V. 2014. A Review of High Volume Low Lime Fly Ash Concrete. International Conference on Biological, Civil and Environmental Engineering BCEE-2014. Dubai UAE.

Yao, Z. T., Ji, X. S., Sarker, P. K., Tang, J. H., Ge, L. Q., Xia, M. S., and Xi, Y. Q. 2015. A Comprehensive Review on the Applications of Coal Fly Ash. Earth-Science Reviews. 141: 105-121.

Cao, D.-z., Selic, E., and Herbell, J.-D. 2008. Utilization of Fly Ash from Coal-fired Power Plants in China. Journal of Zhejiang University Science. 9: 681-687.

Australia, A. D. A. o. 2009. Guide to the Use of Fly Ash in Concrete in Australia. Fly Ash Reference Data Sheet No. 1. Ash Development Association of Australia.

Australia, A. D. A. o. 2009. Australian Experience with Fly Ash in Concrete: Applications and Opportunities. Fly Ash Technical Note No. 8. Ash Development Association of Australia.

Bentz, D. P., Ferraris, C. F., and Snyder, K. A. 2013. Best Practices Guide for High-Volume Fly Ash Concretes. NIST Technical Note 1812.

Obla, K. H. 2008. Specifying Fly Ash for Use in Concrete. Concrete in Focus. 60-66.

Rao, C., Stehly, R. D., and Ardani, A. 2011. Handbook for Proportioning Fly Ash as Cementitious Material in Airfield Pavement Concrete Mixtures, Foundation. I. P. R., Ed. IL, USA. 74.

Rashad, A. M. 2015. A Brief on High-volume Class F Fly Ash as Cement Replacement–A Guide for Civil Engineer. International Journal of Sustainable Built Environment. 4: 278-306.

Thomas, M. 2007. Optimizing the Use of Fly Ash in Concrete. Portland Cement Association Skokie, IL, USA. 5420.

Wesche, K. 2004. Fly Ash In Concrete: Properties and Performance. CRC Press. 7.

Rivera, F., Martínez, P., Castro, J., and López, M. 2015. Massive Volume Fly-ash Concrete: A More Sustainable Material with Fly Ash Replacing Cement and Aggregates. Cement and Concrete Composites. 63: 104-112.

Blanco, F., Garcia, M. P., and Ayala, J. 2005. Variation in Fly Ash Properties with Milling Aand Acid Leaching. Fuel. 84: 89-96.

Fernández-Jiménez, A., and Palomo, A. 2003. Characterisation of Fly Ashes. Potential Reactivity As Alkaline Cements. Fuel. 82: 2259-2265.

Hemalatha, T., Mapa, M., George, N., and Sasmal, S. 2016. Physico-chemical and Mechanical Characterization of High Volume Fly Ash Incorporated and Engineered Cement System Towards Developing Greener Cement. Journal of Cleaner Production. 125: 268-281.

Jones, M., McCarthy, A., and Booth, A. 2006. Characteristics of the Ultrafine Component of Fly Ash. Fuel. 85: 2250-2259.

Romagnoli, M., Sassatelli, P., Lassinantti Gualtieri, M., and Tari, G. 2014. Rheological Characterization of Fly Ash-based Suspensions. Construction and Building Materials. 65: 526-534.

Siddique, R. 2004. Performance Characteristics of High-Volume Class Fly Ash Concrete. Cement and Concrete Research. 34: 487-493.

Supit, S. W. M., Shaikh, F. U. A., and Sarker, P. K. 2014. Effect of Ultrafine Fly Ash on Mechanical Properties of High Volume Fly Ash Mortar. Construction and Building Materials. 51: 278-286.

Wang, X.-Y. 2014. Effect of Fly Ash on Properties Evolution of Cement Based Materials. Construction and Building Materials. 69: 32-40.

Antoni, Gunawan, R., and Hardjito, D. 2015. Rapid Indicators in Detecting Variation of Fly Ash for Making HVFA Concrete. Applied Mechanics and Materials. 815: 153-157.

Antoni, Satrya, V. and Hardjito, D. 2015. Simple Mechanical Beneficiation Method of Coarse Fly Ash with High LOI for Making HVFA Mortar. Civil Engineering Dimension. 17.

Blanco, F., Garcia, M. P., Ayala, J., Mayoral, G., and Garcia, M. A. 2006. The Effect of Mechanically and Chemically Activated Fly Ashes on Mortar Properties. Fuel. 85: 2018-2026.

Shaikh, F. U. A., and Supit, S. W. M. 2015. Compressive Strength and Durability Properties of High Volume Fly Ash HVFA Concretes Containing Ultrafine Fly Ash UFFA. Construction and Building Materials. 82: 192-205.

Hela, R., Tazky, M., & Bodnarova, L. 2016. Possibilities of Determination of Optimal Dosage of Power Plant Fly Ash for Concrete. Jurnal Teknologi. 78(5-3).

Yazici, Ş., and Arel, H. Ş. 2012. Effects of Fly Ash Fineness on the Mechanical Properties of Concrete. Sadhana. 37: 389-403.

Nawaz, A., Julnipitawong, P., Krammart, P., and Tangtermsirikul, S. 2016. Effect and Limitation of Free Lime Content in Cement-fly Ash Mixtures, Construction and Building Materials. 102: 515-530.

Tkaczewska, E. 2014. Effect of the Superplasticizer Type on the Properties of the Fly Ash Blended Cement. Construction and Building Materials. 70: 388-393.

ASTM. 2005. C778, Standard Specification For Standard Sand. ASTM International.

ASTM. 2003. D5239, Standard Practice for Characterizing Fly Ash for Use in Soil Stabilization. American Society for Testing and Materials. ASTM International, West Conshohocken, PA, USA.

ASTM. 2008. C 230, Standard Specification for Flow Table for Use in Tests of Hydraulic Cement. ASTM International, West Conshohocken, PA.

ASTM. 2014. C1679, Standard Practice for Measuring Hydration Kinetics of Hydraulic Cementitious Mixtures Using Isothermal Calorimetry. ASTM International, West Conshohocken, PA,.

ASTM. 2003. C618, Standard Specification for Fly Ash and Raw or Calcined Natural Pozzolan for Use as a Mineral Admixture in Portland Cement Concrete, ASTM International, West Conshohocken, PA.




DOI: http://dx.doi.org/10.11113/jt.v79.11870

Refbacks

  • There are currently no refbacks.


Copyright © 2012 Penerbit UTM Press, Universiti Teknologi Malaysia.
Disclaimer : This website has been updated to the best of our knowledge to be accurate. However, Universiti Teknologi Malaysia shall not be liable for any loss or damage caused by the usage of any information obtained from this web site.
Best viewed: Mozilla Firefox 4.0 & Google Chrome at 1024 × 768 resolution.